Activation of oil palm empty bunches with hydrochloride acid & phosphoric acid and characterization based SNI No. 06-3730-1995

Irna Diah Mumpuni, Mamay Maslahat, Devy Susanty

Abstract


Activated carbon is a solid product resulting from carbonization and activation of lignocellulosic biomass by several methods and activators. Each activator can produce different characteristics of activated carbon. The activated carbon of Oil Palm Empty Fruit Bunches (OPEFB) is processed from Empty Fruit Bunches (EFB) waste, which is quite abundant in Indonesia. The purpose of this study was to determine the characteristics of OPEFB carbon that had been chemically activated using hydrochloric acid (HCl) and phosphoric acid (H3PO4) based on the Indonesian National Standard (SNI) No. 06 - 3730 - 1995. The research method consisted of the process of carbonization of OPEFB using a pyrolysis device at 400oC for 6 hours; activation of carbon with activator HCl and H3PO4 at various activator concentrations; characterization of activated carbon on the parameters of moisture content, ash content, absorption of iodine, and absorption of methylene blue. The results showed that the 0.5000 M HCl was the best activator that produced the quality of OPEFB activated carbon according to SNI 06 - 3730 - 1995 on parameters of moisture content, ash content and absorption of iodine.

Keywords: Activated Carbon, Iodine Absorption, Oil Palm Empty Fruit Bunches

ABSTRAK

Aktivasi karbon tandan kosong kelapa sawit dengan asam klorida dan asam fosfat serta uji karakterisasi berdasarkan SNI No. 06–3730–1995

Karbon aktif merupakan produk padatan yang dihasilkan dari karbonisasi dan aktivasi biomassa lignoselulosa dengan beberapa metode dan aktivator. Masing-masing aktivator dapat menghasilkan karakteristik karbon aktif yang berbeda. Karbon aktif Tandan Kosong Kelapa Sawit (TKKS) diolah dari limbah TKKS yang keberadaannya cukup melimpah di Indonesia. Tujuan penelitian ini adalah mengetahui karakteristik karbon TKKS yang telah diaktivasi secara kimia menggunakan aktivator asam klorida (HCl) dan asam fosfat (H3PO4) berdasarkan Standar Nasional Indonesia  (SNI) No.  06 – 3730 – 1995. Metode penelitian terdiri atas proses karbonisasi TKKS menggunakan alat pirolisis pada suhu 400 ℃ selama 6 jam; aktivasi karbon dengan aktivator HCl dan H3PO4 pada berbagai konsentrasi aktivator; serta karakterisasi karbon aktif pada parameter kadar air dan abu, daya jerap terhadap iod serta daya jerap terhadap biru metilen. Hasil penelitian menunjukkan bahwa HCl 0,5 M merupakan aktivator terbaik dan karbon aktif yang dihasilkan memiliki karakteristik yang sesuai dengan SNI 06 – 3730 – 1995 pada parameter kadar air dan abu serta daya jerap terhadap iod.

Kata kunci: Daya Jerap Iod, Karbon Aktif, Tandan Kosong Kelapa Sawit


Full Text:

PDF

References


ASTM International. (2014). ASTM D4607-14, Standard Test Method for Determination of Iodine Number of Activated Carbon.

ASTM International. West Conshohocken. PA. www.astm.org.

Badan Standar Nasional. (1995). Arang Teknis. SNI 06-3730-1995. Jakarta.

Efiyanti L., Wati, S.A., & Maslahat, M. (2020). Pembuatan dan Analisis Karbon Aktif dari Cangkang Buah Karet dengan Proses Kimia dan Fisika. Jurnal Ilmu Kehutanan, 14(1), 94-108.

Faradina, E. &Setiawati, N. (2010). Regenerasi Minyak Jelantah dengan Proses Bleaching Menggunakan Adsorben Karbon Aktif (Laporan Penelitian). Program Studi Teknik Kimia, Fakultas Teknik, Universitas Lambung Mangkurat, Banjarbaru.

Hardi, A.D., Joni, R., Syukri, & Aziz, H. (2020). Pembuatan Karbon Aktif dari Tandan Kosong Kelapa Sawit sebagai Elektroda Superkapasitor. Jurnal Fisika Unand, 9(4), 479-486.

Kemenperin. (2017). Ekspor Karbon Aktif. https://kemenperin.go.id/statistik/query_komoditi.php? komoditi=activated+carbon&negara=&jenis=e& action= Tampilkan. Diakses September 2019. Kemenperin. 2017. Ekspor karbon aktif https://kemenperin.go.id/statistik/query_komoditi.php? komoditi=activated+carbon&negara=&jenis=e& action= Tampilkan. Diakses September 2019

Kurniati, E. 2008. Pemanfaatan Cangkang Kelapa Sawit Sebagai Karbon Aktif. Jurnal Penelitian Ilmu Taknik, 8 (2), 96 – 103.

Laos, L. E. & Selan, A. (2016). Pemanfaatan Kulit Singkong Sebagai Bahan Baku Karbon Aktif. Jurnal Ilmu Pendidikan Fisika, 1(1), 32 – 36.

Maslahat, M., Arrisujaya, D., & Lismayani, S. (2019). Optimasi Suhu Aktivasi Pada Pembuatan Arang Aktif Berbahan Dasar Limbah Tandan Kosong Kelapa Sawit. Prosiding Seminar Lignoselulosa ,46-51.

Meisrilestari, Y., Khomaini,R., & Wijayanti, H. (2013). Pembuatan Karbon Aktif Dari Cangkang Kelapa Sawit Dengan Aktivasi Secara Fisika, Kimia dan Fisika-Kimia. Jurnal Konversi, 2(1), 46 – 51.

Miranti, S. T. (2012). Pembuatan Karbon Aktif dari Bambu dengan Metode Aktivasi Terkontrol Menggunakan Activating Agent H3PO4 dan KOH (Skripsi). Fakultas Teknik, Universitas Indonesia. Depok.

Pakpahan, H., Manurung, G. ME., & Yulia, A. E. (2013). Aplikasi Kompos Tandan Kosong Kelapa Sawit (Elaeis guineensis Jacq) Terhadap Pertumbuhan Bibit Kelapa Sawit Di Pembibitan Utama. Agro Technology. Fakultas Pertanian. Riau.

Pari, G. (2007). Teknologi Pembuatan dan Uji Mutu Arang, Briket Arang, dan Karbon Aktif. Seminar Tenaga Teknis Penguji HHBK. Pusat Penelitian dan Pengembangan Hasil Hutan. Palembang

Rachmani, F. K. & Sudibandriyo, M. (2014). Pemanfaatan Tandan Kosong Kelapa Sawit Untuk Produksi Karbon Aktif dengan Aktivasi Kimia. Fakultas Teknik. Universitas Indonesia. Depok.

Rahayu, A. N., & Adhitiyawarman. (2014). Pemanfaatan Tongkol Jagung Sebagai Adsorben Besi Pada Air Tanah. JKK, 3(3), 7 – 13.

Ramdja, A. F., Halim, M., & Handi, J. (2008). Pembuatan Karbon Aktif dari Pelepah Kelapa (Cocos nucifera). Jurnal Teknik Kimia, 15 (2).

Sahara, E., Dahliani, N. K., & Manuaba, I. B. P. (2017). Pembuatan dan Karakterisasi Karbon Aktif dari Batang Tanaman Gumitir (Tagetes erecta) yang Diaktivasi dengan Aktivator NaOH. Jurnal Kimia, 11(1), 174 – 180.

Sahara, E., Sulihingtyas, W.D. & Mahardika, I. P. A. D. S. (2017). Pembuatan dan Karakterisasi Karbon Aktif dari Batang Tanaman Gumitir (Tagetes erecta) yang Diaktivasi dengan H3PO4. Jurnal Kimia, 11(1), 1 – 9.

Subadra, I., Setiaji, B., & Tahir, I. Activated Carbon Production from Coconut Shell With (NH4)HCO3 Activator As An Adsorbent in Virgin Coconut Oil Purification. Prosiding Seminar Nasional DIES, 1 – 8. Universitas Gajah Mada.

Tryana, M., & Sarma, T. (2003). Karbon Aktif (Pengenalan dan Proses Pembuatannya). Jurnal Kimia, 1-9.




DOI: https://doi.org/10.31938/jsn.v11i1.291

Refbacks

  • There are currently no refbacks.


Copyright (c) 2021 Jurnal Sains Natural

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

 

Lisensi Creative Commons
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.

Indexed by:

View The Statistics of J. Sains Nat.