PRESIPITASI LOGAM BERAT LIMBAH CAIR LABORATORIUM MENGGUNAKAN NATRIUM SULFIDA DARI BELERANG ALAM

Wisni Rona Anami, Mamay Maslahat, Dian Arrisujaya

Abstract


Precipitation of Laboratory Wastewater Heavy Metals by Natural Sulphur Sodium Sulfide 

Sodium sulfide (Na2S) from natural sulfur has been used for heavy metal precipitation from laboratory wastewater. Heavy metals in laboratory wastewater include mercury (Hg), lead (Pb), chromium (Cr) and zinc (Zn). Initial laboratory wastewater testing was performed by measuring the initial pH and the concentration of heavy metals in the wastewater prior to precipitation using the atomic absorption spectrophotometer. Sulphide precipitation phase consists of variations in the concentration of NaOH, time, temperature, and volume of dissolving Na2S. Parameters for the efficiency of Hg, Pb, Zn and Cr heavy metal precipitation were the initial pH, concentration and rate of stirring of the solution. Results showed that the optimum precipitation efficiency for Zn is achieved by using 10 % Na2S solution with an efficiency of 97.93 %. The most significant reduction in Cr and Hg was the use of 20 % Na2S solution with a precipitation efficiency of 99.24 % and 99.76 % respectively. The optimal efficiency for Pb with a 30 % Na2S solution was 99.68 %. Natural sulfur can reduce the levels of heavy metals in laboratory wastewater by precipitation.

Key words: Natural sulfur, Heavy metals, Precipitation, Sodium sulfide,

 

ABSTRAK

Presipitasi logam berat dari limbah cair laboratorium telah dilakukan dengan menggunakan natrium sulfida (Na2S) dari belerang alam. Logam berat yang terkandung dalam limbah cair laboratorium diantaranya adalah merkuri (Hg), timbal (Pb), kromium (Cr) dan seng (Zn). Pengujian awal limbah laboratorium dilakukan dengan mengukur pH awal dan kadar  logam  berat  yang  terdapat  dalam  limbah sebelum presipitasi menggunakan pH meter dan spektrofotometer serapan atom. Tahapan presipitasi limbah oleh sulfida meliputi pembuatan variasi konsentrasi NaOH, waktu, suhu, dan volume pelarutan Na2S. Parameter efisiensi presipitasi logam Hg, Pb, Zn, dan Cr meliputi pH, Konsentrasi dan Kecepatan pengadukan. Hasil  penelitian  menunjukkan  efisiensi pengendapan optimal untuk logam Zn terdapat pada penggunaan larutan Na2S 10% dengan efisiensi 97,93%. Larutan Na2S 20% paling banyak menurunkan logam Cr dan Hg dengan efisiensi masing-masing sebesar 99,24% dan99,76%. Efisiensi optimal untuk logam Pb berada pada penggunaan larutan Na2S 30% dengan efisiensi 99,68%. Belerang  alam  mampu  menurunkan kadar logam berat dalam limbah cair laboratorium dengan metode presipitasi.

Kata kunci: Belerang alam, Logam berat, Presipitasi, Natrium sulfida


Full Text:

PDF

References


Adli, H. 2012. Pengolahan Limbah Cair Laboratorium dengan Metode Presipitasi dan Adsoprsi untuk Penurunan Kadar Logam Berat. Skripsi. Universitas Indonesia. Depok.

Amer, S.I. 1998. Treating Metal Finishing Wastewater. Aquachem. Canton.

Andaka, G. 2008. Penurunan Kadar Tembaga pada Limbah Cair Industri Kerajinan Perak dengan Presipitasi Menggunakan Natrium Hidroksida. Jurnal Teknologi 1 (2):109-224

Asmadi, S. Endro, W. Oktiawan. Pengurangan Chrom (Cr) dalam Limbah Cair Industri Kulit pada Proses Tannery Menggunakan Senyawa Alkali Ca(OH)2, NaOH dan NaHCO3. Jurnal Air Indonesia 5 (1): 41-54

Asri, N. P., R. Abadi, A. Hasmawati, S. A. Mubarok. 2010. Penurunan Kadar Logam Berat Limbah Cair Industri Emas (PT. X) di Surabaya. Jurnal Teknik Kimia Indonesia 9(2): 55-61

Barbooti M.M, B.A. Abid, N.M. Al-Shuwaiki 2011. Removal of heavy metals usi.ng chemicals precipitation. Eng. & Tech. Journal 29 (3): 595 – 612

Cucikodana, Y., A. Supriadi, B. Purwanto. 2012. Pengaruh Perbedaan Suhu Perebusan dan Konsentrasi NaOH terhadap Kualitas Bubuk Tulang Ikan Gabus (Channa striata). Jurnal Fishtech 1 (1):91-101

Day, R.A dan A.L Underwood. 2002. Analisis Kimia Kuantitatif. Edisi ke Enam. Erlangga. Jakarta.

Fadlilah, I., Prasetya,A., Mulyono, P. 2018. Recovery Ion Hg2+ dari Limbah Cair Industri Penambangan Emas Rakyat dengan Metode Presipitasi Sulfida dan Hidroksida. Jurnal Rekayasa Proses 12 (1): 23-31

Hagemann, S., U. Oppermann, T. Brasser. 2014. Behaviour of Mercury and Mercury Compounds at The Underground Disposal In Salt Formations and Their Potential Mobilisation By Saline Solutions. Federal Environment Agency Germany. Umweltbundesamt

Handoko, C.T., Yanti, T.B., Syadiyah, H., Marwati, S. 2013. Penggunaan Metode Presipitasi untuk Menurunkan Kadar Cu dalam Limbah Cair Industri Perak di Kota Gede. Jurnal Penelitian Saintek. 18 (2):51-58

Ismayana, A. 1997. Proses Presipitasi Kimia sebagai Pengolahan Air Buangan Lanjut Senyawa Ortofosfat. Tesis. Institut Teknologi Bandung. Bandung.

Khopkar, S.M. 2007. Konsep Dasar Kimia Analitik. Diterjemahkan oleh A. Saptorahardjo. UI Press. Jakarta

La Grega. 2001. Hazardous Waste Management. Mc Graw Hill Inc. New York.

Lewis, A. and R.V. Hille. 2006. An Exploration Into The Sulphide Precipitation Method and Its Effect on Metal Sulphide Removal. Hydrometallurgy Joural 81(3):197-204.

Lusiani, T. 2011. Pengolahan Limbah Cair yang Mengandung Logam Merkuri dengan reaksi Fenton dan Presipitasi Sulfida. Skripsi. Institut Pertanian Bogor. Bogor.

Munfarida, A, A. T. S. Haji, L. D. Susanawati, H. B. Cahyono. 2016. Reduksi Logam Merkuri (Hg) dengan Penambahan Na2S atau NaOH pada Limbah Cair Pengujian COD Refluk Terbuka. Jurnal Sumberdaya Alam dan Lingkungan 1(1):71-77.

Naim, R., L. Kisay, J. Park, M. Qaisar, A.B. Zulfiqar, M. Noshin, K. Jamil. 2010. Precipitation chelation of cyanide complexes in electroplating industry wastewater. International Journal of Environment Research. 4(4):735-740

Peraturan Menteri Lngkungan Hidup No. 5 Tahun 2014 Tentang Baku Mutu Air Limbah.

Sidik, A. A. dan E. Damanhuri. Studi Pengelolaan Limbah B3 (Bahan Berbahaya dan Beracun) Laboratorium-Laboratorium di ITB. Jurnal Teknik Lingkungan 18 (1):12-20

Skants, C. dan A. Jamali. 2012. Evaluation of Treatment Techniques for Mercury Contaminated Leachates. Thesis. Master of Science. Chalmers University of Technology

Widowati, W., A. Sastiono, R. Jusuf. 2008. Efek Toksik Logam Pencegahan dan Penanggulangan Pencemaran. Penerbit Andi. Yogyakarta




DOI: https://doi.org/10.31938/jsn.v10i2.283

Refbacks

  • There are currently no refbacks.


Copyright (c) 2020 Jurnal Sains Natural

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

 

Lisensi Creative Commons
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.

Indexed by:

View The Statistics of J. Sains Nat.